Investment materials are thermally-resistant compounds for fabricating refractory dies (for all-ceramic veneers, inlays) or models (for CoCr) and accurately investing objects for sintering, pressing (ceramic), soldering or casting. They are mixed from powder and liquid to a plastic/fluid consistency – investments for use when casting and with pressed ceramics are often mixed in a vacuum mixer and soldering investments spatulated by hand.
The powder is made up of 80 - 85 % quartz modifications (SiO2, silicon dioxide, e.g. cristobalite) and their relative proportions determine the thermal expansion. Larger and smaller, rounded and sharp-edged grains provide for a balance between the desired properties of crack-resistance and smooth surfaces.
Binders make up the remaining 15 - 20 % of the powder. Apart from plaster, silicate and acetate-bonded investments, phosphate-bonded materials are mostly used nowadays. They contain approximately equal parts of magnesium oxide (MgO) and monoammonium phosphate (MAP) and govern not only the flowability, but also the setting properties such as setting temperature, time and expansion.
Depending on which material is being invested – particularly when casting fixed restorations with precious or non-precious alloys as well as removable CoCrMo dentures – it is essential to accurately control the expansion of the investment in order to compensate for thermal contraction (approx. 1.5 % - 2.5 %) of the molten alloy during solidification. Investments undergo both thermal and setting expansion. Assuming all other conditions remain unchanged, the setting expansion is determined by the mixing ratio of distilled (or demineralised) water to investment mixing liquid. It contains silica sol particles which function as hardeners and expansive fillers by gelling and crystallising the investment during setting to create a stable, pressure and fracture-resistant form. Investments for use when casting titanium must be prevented from reacting with the molten titanium – previously by means of so-called "refractory oxides" now superseded by spinel and acetate-based binders.
Previously, micrograin investment containing soluble glass binder (and possibly grain refiners for enhancing the structure) was used when casting CoCr for protecting the surfaces of wax patterns against the effects of reversible hydrocolloid duplicating materials. This is no longer required for today's silicone duplicating materials. Classic lost-wax casting involves spruing the wax pattern onto a crucible former and coating it with wetting agent to avoid entrapping air in the investment. A metal (or removable plastic) casting ring limits the expansion transversely (avoids excessive expansion) and a casting ring liner ("ceramic fibre") defines the space available. The investment is then mixed briefly on a vibrator and poured into the ring. The investment sets/hardens in 15 - 40 minutes. When using modern (speed casting) investments it is essential to drive off the residual water in a preheating furnace before final set and without causing cracks. Thermal expansion of the investment is completed by preheating it to a temperature which prevents the molten alloy cooling prematurely and enables it to flow into intricately detailed areas. In order to produce accurate castings, an investment must reproduce details crisply, exhibit smooth surfaces, resist corrosion of the molten alloy despite the high temperatures, not contract during the casting dwell period, be sufficiently porous to enable gases to escape and easily devested. In addition, after casting/pressing and cooling the investment mould (CoCr: also the duplicate model) has to be split open/sandblasted and, consequently, destroyed in order to devest the casting. Just as when mixing, as little respirable quartz dust as possible should be created during devesting which Is why modern investments are low-dust.
Von uns erhalten Sie professionelle Unterstützung.
Treten Sie mit uns in Kontakt oder nutzen Sie unser Kontaktformular.
Deutsch | Englisch |
---|---|
Alveolarkamm-Abhang | ridge slope |
Implantat-Suprakonstruktionen Implantat-Suprakonstruktionen Ober- und Unterkiefertotalprothese (Unterseite, mit Kugelkopfmatrizen)
Kugelkopf Eine S. kann rein implantatgetragen sein oder sich sowohl auf Zähnen, als auch auf Implantaten abstützen. Insbesondere bei Brücken spricht man dann von Hybrid- oder Verbund-Zahnersatz. Metallkeramikkronen auf Implantaten Bei zementierten S. ist zwischen provisorischer (temporärer), definitiver (permanenter) und semi-permanenter Zementierung zu unterscheiden. Letztere soll eine sichere Befestigung und gleichzeitig das Abnehmen der S. durch den Zahnarzt im Bedarfsfall ermöglichen. Damit handelt es sich um eine sogenannte bedingt abnehmbare (für den Patienten also festsitzende) S. Dazu gehören auch die verschraubten S. Die beiden Befestigungsarten bieten Vor- und Nachteile: Verschraubungen bedingen Spalträume, die bakteriell besiedelt werden können, zur Vorbeugung dagegen werden spezielle Gele zum Einbringen in den Implantat-Innenraum angeboten, die langfristig wirksam bleiben sollen. Erfolgt eine Fixation von S. mit Schrauben, können bei diesen auch Misserfolge durch Lockerung, Überlastung und Bruch auftreten. Da Implantate keine Eigenbeweglichkeit aufweisen und starr im Kieferknochen verankert sind, wird stets ein spannungsfreier Sitz von S. angestrebt. Er kann bei verschraubten S. auf mindestens zwei Pfeilern mit dem Sheffield-Test (spaltfreier Sitz bei Anziehen einer beliebigen Einzelschraube) überprüft werden. Um spannungsfreie Gerüste herzustellen, werden Verfahren zur intraoralen Verbindung (etwa Verkleben) von Teilen der S. und/oder zur digitalen Fertigung (z.B. Fräsen, Sintern) angewendet. Um unzugängliche Zementüberschüsse, die zu Periimplantitis und Implantatverlust führen können, zu vermeiden, sollte der Restaurationsrand zementierter S. stets im Bereich des Zahnfleischrands enden. Dies lässt sich – vor allem bei Implantatplattformen auf Knochenniveau ("bone level") mit entsprechenden (ggf. individuell angefertigten) Abutments erreichen. Abutments dienen als Verbindung zwischen Implantaten und S. Bei S. auf mehreren Pfeilern ermöglichen abgewinkelte Formen die Parallelisierung hin zu einer gemeinsamen Einschubrichtung. Abutments können entweder die Form eines präparierten Zahnstumpfs nachahmen oder eine Komponente eines Verbindungselements (z.B. Druckknopfsysteme, Kugelköpfe, Stege, Magnete) beinhalten. Die S. umfasst in diesen Fällen die entsprechenden ergänzenden Komponenten. |