Impression materials
Dental impression materials are used for taking impressions in the mouth. They are intended for reproducing and transferring the outer contours of intraoral structures (teeth, jaws, soft tissues, fillings, restorations) three-dimensionally during impression-taking. An initially soft material is applied directly to the surface, avoiding air voids where possible, before setting rapidly (between one and a few minutes) in a supporting impression tray to create a female mould (impression). The impression is then cast (usually with plaster but possibly with acrylic resin) to produce a model.
In the past, plaster was used for taking impressions even though it was not elastic after setting. For this reason, a plaster impression of undercut structures (teeth) always had to be sectioned (fractured) in order to withdraw it from the mouth. Impression plaster was also used as a pick-up impression material for single-prep impressions taken using customised copper rings filled with thermoplastic (resin-based) impression material. However, after cooling and setting the rigid impression could not be removed from undercuts without being damaged.
For this reason, nowadays rigid setting, reversible thermoplastic materials are only used in non-undercut regions, e.g., resins for functional impressions on denture peripheries or waxes for bite registration.
Special zinc-oxide-eugenol impression materials may also be used when taking functional impressions.
For decades almost only impression materials which remain elastic after setting and, when sufficiently thick, virtually fully recover their original shape after removal from the mouth, have been in use. This property is referred to as “elastic recovery”.
These include alginate impression materials which, when mixed with water, form gel-like polysaccharides. As alginate impressions may dry out or absorb further water and swell, they are neither dimensionally stable nor can they be stored for longer periods. This also applies to reversible hydrocolloids.
In the meantime, so-called elastomeric alginates, which are generally irreversible materials and set to a rubbery-elastic consistency, are widely accepted. The chemistry behind the chain reactions can be divided into polymerization (e.g. polyether impression materials), polyaddition (e.g. A-silicones) and polycondensation (e.g. C-silicones, polysulfides). These impression materials are either mixed by hand or mechanically (refer to “Mixing systems for impression materials”) to combine two components (“base” and “catalyst”) homogeneously and void-free.
One-step putty-wash impression taken with regular and light body silicones over impression posts
Silicone impression materials (polyvinyl siloxanes, PVS) in particular are supplied in different consistencies for various impression procedures. When taking one-step or two-step putty-wash impressions, a kneadable (heavy body) putty exerts controlled pressure (usually in an impression tray) on a syringeable, light body, low viscosity precision impression material. This allows it to penetrate narrow gaps (e.g., intraorally in the gingival sulcus, interdental spaces, fissures) thus increasing the accuracy of detail (crispness) of the precision impression.
Materials which are also kneadable yet slightly less viscous, and with an extended setting time, are used for taking functional impressions for full dentures. They intentionally displace very compressible mucosal areas more than firm sections (varying mucosal resilience) thus balancing the pressure exerted which reduces the risk of denture sores.
Regular body silicone impression materials are either used with other materials or alone (monophase) e.g., for taking pick-up impressions for fixed/removable restorations either involving implants or not.
Pick-up impression taken over inner telescopes using monophase silicone
To ensure that the impression material flows smoothly onto surfaces, which are often moist, a degree of hydrophilicity (acute contact angle) is desirable.
The setting reaction of impression materials may be accelerated by specific additives or a warmer environment (e.g., intraoral) but can also be retarded by inhibitors or precooling. Processing encompasses the mixing time, working time (loading the tray with impression material and inserting it into the mouth) and setting time. Special chromatic impression materials change colour to indicate the changes.
Silicone impression materials which attain their final hardness very quickly can also be used for bite registration.
Nowadays, materials for analogue impressions are often no longer required as contactless optical procedures using intraoral scanners are increasingly in use (digital impression-taking).
Von uns erhalten Sie professionelle Unterstützung.
Treten Sie mit uns in Kontakt oder nutzen Sie unser Kontaktformular.
Deutsch | Englisch |
---|---|
Alveolarkamm-Abhang | ridge slope |
Implantat-Suprakonstruktionen Implantat-Suprakonstruktionen Ober- und Unterkiefertotalprothese (Unterseite, mit Kugelkopfmatrizen)
Kugelkopf Eine S. kann rein implantatgetragen sein oder sich sowohl auf Zähnen, als auch auf Implantaten abstützen. Insbesondere bei Brücken spricht man dann von Hybrid- oder Verbund-Zahnersatz. Metallkeramikkronen auf Implantaten Bei zementierten S. ist zwischen provisorischer (temporärer), definitiver (permanenter) und semi-permanenter Zementierung zu unterscheiden. Letztere soll eine sichere Befestigung und gleichzeitig das Abnehmen der S. durch den Zahnarzt im Bedarfsfall ermöglichen. Damit handelt es sich um eine sogenannte bedingt abnehmbare (für den Patienten also festsitzende) S. Dazu gehören auch die verschraubten S. Die beiden Befestigungsarten bieten Vor- und Nachteile: Verschraubungen bedingen Spalträume, die bakteriell besiedelt werden können, zur Vorbeugung dagegen werden spezielle Gele zum Einbringen in den Implantat-Innenraum angeboten, die langfristig wirksam bleiben sollen. Erfolgt eine Fixation von S. mit Schrauben, können bei diesen auch Misserfolge durch Lockerung, Überlastung und Bruch auftreten. Da Implantate keine Eigenbeweglichkeit aufweisen und starr im Kieferknochen verankert sind, wird stets ein spannungsfreier Sitz von S. angestrebt. Er kann bei verschraubten S. auf mindestens zwei Pfeilern mit dem Sheffield-Test (spaltfreier Sitz bei Anziehen einer beliebigen Einzelschraube) überprüft werden. Um spannungsfreie Gerüste herzustellen, werden Verfahren zur intraoralen Verbindung (etwa Verkleben) von Teilen der S. und/oder zur digitalen Fertigung (z.B. Fräsen, Sintern) angewendet. Um unzugängliche Zementüberschüsse, die zu Periimplantitis und Implantatverlust führen können, zu vermeiden, sollte der Restaurationsrand zementierter S. stets im Bereich des Zahnfleischrands enden. Dies lässt sich – vor allem bei Implantatplattformen auf Knochenniveau ("bone level") mit entsprechenden (ggf. individuell angefertigten) Abutments erreichen. Abutments dienen als Verbindung zwischen Implantaten und S. Bei S. auf mehreren Pfeilern ermöglichen abgewinkelte Formen die Parallelisierung hin zu einer gemeinsamen Einschubrichtung. Abutments können entweder die Form eines präparierten Zahnstumpfs nachahmen oder eine Komponente eines Verbindungselements (z.B. Druckknopfsysteme, Kugelköpfe, Stege, Magnete) beinhalten. Die S. umfasst in diesen Fällen die entsprechenden ergänzenden Komponenten. |